Conversione Durezze

HV–HRC e HRC-HV-HB-HRA-HRB-Rm per acciai al carbonio e legati. Secondo Tabella ASTM A 370 – 03a

HV HRC HV HRC HV HRC HV HRC HV HRC
2270 85 1950 81 1633 77 1323 73 1004 69
2190 84 1865 80 1556 76 1245 72 940 68
2110 83 1787 79 1478 75 1160 71 920 67,5
2030 82 1710 78 1400 74 1076 70 900 67
HRC
Cono diamante
HV
Vickers 30
HB
Brinell 3000 Kgf
HRA
Cono diamante
Rm
N/mm2 MPa
HRB
Sfera 1/16’’
HV
Vickers 30
HB
Brinell 3000 Kgf
HRA
Cono diamante
Rm
N/mm2 MPa
68 940 85.6 100 240 240 61.5 800
67 900 85.0 99 234 234 60.9 785
66 865 84.5 98 228 228 60.2 750
65 832 739 83.9 97 222 222 59.5 715
64 800 722 83.4 96 216 216 58.9 705
63 772 706 82.8 95 210 210 58.3 690
62 746 688 82.3 94 205 205 57.6 675
61 720 670 81.8 93 200 200 57.0 650
60 697 654 81.2 92 195 195 56.4 635
59 674 634 80.7 2420 91 190 190 55.8 620
58 653 615 80.1 2330 90 185 185 55.2 615
57 633 595 79.6 2240 89 180 180 54.6 605
56 613 577 79.0 2160 88 176 176 54.0 590
55 595 560 78.5 2070 87 172 172 53.4 580
54 577 543 78.0 2010 86 169 169 52.8 570
53 560 525 77.4 1950 85 165 165 52.3 565
52 544 512 76.8 1880 84 162 162 51.7 560
51 528 496 76.3 1820 83 159 159 51.1 550
50 513 482 75.9 1760 82 156 156 50.6 530
49 498 468 75.2 1700 81 153 153 50.0 505
48 484 455 74.7 1640 80 150 150 49.5 495
47 471 442 74.1 1580 79 147 147 48.9 485
46 458 432 73.6 1520 78 144 144 48.4 475
45 446 421 73.1 1480 77 141 141 47.9 470
44 434 409 72.5 1430 76 139 139 47.3 460
43 423 400 72.0 1390 75 137 137 46.8 455
42 412 390 71.5 1340 74 135 135 46.3 450
41 402 381 70.9 1300 73 132 132 45.8 440
40 392 371 70.4 1250 72 130 130 45.3 435
39 382 362 69.9 1220 71 127 127 44.8 425
38 372 353 69.4 1180 70 125 125 44.3 420
37 363 344 68.9 1140 69 123 123 43.8 415
36 354 336 68.4 1110 68 121 121 43.3 405
35 345 327 67.9 1080 67 119 119 42.8 400
34 336 319 67.4 1050 66 117 117 42.3 395
33 327 311 66.8 1030 65 116 116 41.8 385
32 318 301 66.3 1010 64 114 114 41.4
31 310 294 65.8 970 63 112 112 40.9
30 302 286 65.3 950 62 110 110 40.4 370
29 294 279 64.6 930 61 108 108 40.0
28 286 271 64.3 900 60 107 107 39.5
27 279 264 63.8 880 59 106 106 39.0 360
26 272 258 63.3 860 58 104 104 38.6
25 266 253 62.8 850 57 103 103 38.1 350
24 260 247 62.4 820 56 101 101 37.7
23 254 243 62.0 810 55 100 100 37.2 340
22 248 237 61.5 790 54 36.8
21 243 231 61.0 770 51 94 35.5 330
20 238 226 60.5 760 49 92 34.6 320
I valori in grassetto sono fuori tabella ASTM ma comunque attendibili I valori in corsivo sono dovuti al passaggio da tab. 2 a tab. 3 della Norma ASTM A 370
Durezza Rockwell HRC cono diamante 120° carico 1470 N (150 Kgf) durata 30’’ Durezza Rockwell HRA cono diamante carico 588 N (60 Kgf) durata 30’’
Durezza Vickers HV piramide diamante 136° Carico 294 N (30 Kgf) durata 15’’ Durezza Rockwell HRB sfera 1/16’’ carico 980 N (100 Kgf) durata 30’’
Durezza Brinell HB sfera 10 mm carico 29.400N (3000 Kgf) durata carico 15’’ Resistenza a trazione Rm N/mm2 (Mpa)